Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of RAVAMID® B GB20 BK45 - PA6-GB20 - Ravago Group

Material Data Center offers the following functions for RAVAMID® B GB20 BK45:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Ravamid B datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics値単位テスト基準
ASTM数据
成形収縮率., 平行 0.01 mm/mm ASTM D 955
機械的特性値単位テスト基準
ISO データ
引張弾性率 3200 MPa ISO 527
降伏応力 65 MPa ISO 527
破壊応力 60 MPa ISO 527
破壊ひずみ 25 % ISO 527
曲げ弾性率, 23°C 2600 MPa ISO 178
シャルピー衝撃強さ, +23°C 45 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 5.5 kJ/m² ISO 179/1eA
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 75[ann.] °C ISO 75-1/-2
ビカット軟化温度, B 200 °C ISO 306
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.6 mm -
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 3.2 mm -
燃焼速度, FMVSS, 1mm厚 100 mm/min ISO 3795 (FMVSS 302)
グローワイヤ燃焼性指数 (GWFI) 650 °C IEC 60695-2-12
GWFI - 試験片の厚さ 2 mm -
ann.: annealed
その他の特性.値単位テスト基準
吸湿率 0.15 % Sim. to ISO 62
密度. 1280 kg/m³ ISO 1183
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 75 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.12 % -
樹脂温度 240 - 270 °C -
金型温度 70 - 90 °C -
Zone 1 220 - 230 °C -
Zone 2 230 - 245 °C -
Zone 3 250 - 260 °C -
Nozzle temperature 250 - 260 °C -
Screw speed 50 - 80 rpm -
Back pressure 0.4 - 0.8 MPa -
後硬化時間 6 - 8 MPa -
特殊な特性
成形加工法.
射出成形.
納入形状.
黒
領域別の利用可能性
ヨーロッパ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.